◆ Performance and scope of application ◆ 
 1, for PA6, TPU, the ABS, EPDM 
 GK-8 is the intercalating agent intercalated match with caprolactam series of modified nano-montmorillonite, melt blending of PA6, TPU, the ABS, EPDM modified. GK-8 molten material to form a nanocomposite nanocomposites, its performance is to improve the mechanical properties of polymer materials, the material impact performance does not reduce, but also can effectively improve the flame retardant properties of the material and can improve the material dripping during combustion phenomenon. 
 For PET and engineering plastics, PET / PBT alloy 
 PET in the crystallization process must complete the conversion from the cis-trans configuration, therefore, the crystallization speed is very slow, the product due to contraction lead to warpage, high rejection rate. The use of polyester nanocomposite additive, significantly increase the crystallization rate of PET at the same time, you can also improve the stiffness and temperature of the substrate, substantially reduce the warpage of the finished product, after contraction, and significantly improve the yield. 
 ◆ use ◆ 
 1, for PA6, TPU, the ABS, EPDM 
 GK-8 dispersion mixer, mixer and twin-screw extruder. Can also be made with nylon 6 masterbatch later compound materials. 
 Steps: mix material --- twin-screw extrusion granulation - the masterbatch and particle blends --- together with the rest of materials and granulation. Among them, the rubber blends steps as follows: mixed refining --- banburying ----- do finished 
 ◆ performance ◆ 
 Series GK - 8 
 Appearance White 
 Specific Gravity (g/cm3) 1.8-2.0 
 Humidity of ≤ 5% 
 Interlayer spacing (d001) 1.9-2.4 nm 
 Maximum processing temperature (° C) 260 
 2, for PET plastic, PET, / of PBT alloy 
 Use: according to the manufacturer's original formula, on this basis, join the PET nanocomposite additive common mixed in the twin-screw granulator granulator. Original blend composition of all particles, the particles need to be added to 0.1% -0.2% of liquid paraffin, mix, then add additive blending, granulation. 
 Application of results: 
 Add the GK-8 nanocomposite mechanical properties, thermal properties, barrier properties has greatly improved and can be formed with the Department of phosphorus and nitrogen or phosphorus flame retardant compound, together to improve the flame retardancy. Can be used in conjunction with fiberglass to cover the drain-fiber composite material can be made to do the film. Added :2-15%.